Low Alloy Tool Steel Bar, DIN 105cr4
Wuxi Taixie Metal Material Co., Ltd.- Technique:Hot Rolled
- Composition:Ferrous Steel Scrap
- Standard:AISI, ASTM, DIN, JIS, GB
- Type:Special Steel Bar
- Shape:Bar
- Surface Treatment:Polished
Base Info
- Transport Package:Woven Bag, Wooden Box
- OEM:Yes
- Delivery Time:5~10 Working Days
- Yield Strength:225
- Certificate:ISO SGS
- Poisson′s Ratio:0.25~0.33
- Strength:375-500
- Elongation:25
- Application:Tool Steel Bar
- Special Use:High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
- Model NO.:ASB6
- Specification:ISO SGS
- Trademark:Taixie
- Origin:Wuxi, Jiangsu
- HS Code:7507120000
- Production Capacity:10000tons,Y
Description
Basic Info.
Model NO. ASB6 Special Use High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel Application Tool Steel Bar Elongation 25 Strength 375-500 Poisson′s Ratio 0.25~0.33 Certificate ISO SGS OEM Yes Delivery Time 5~10 Working Days Yield Strength 225 Transport Package Woven Bag, Wooden Box Specification ISO SGS Trademark Taixie Origin Wuxi, Jiangsu HS Code 7507120000 Production Capacity 10000tons/YProduct Description
Key Specifications/Special Features:Description
Low alloyed cold working tool steel.
Applications
For balls, rollers, links with diameter up to 10-17mm.
Chemical composition (in weight%)
C 1.05
Si 0.25
Mn 0.33
Cr 1.03
Physical properties (average values) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing
Heat to 720-760ºC, cool slowly in furnace. This will produce a maximum Brinell hardness of 207.
Normalizing
Temperature: 860-890ºC.
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650ºC, holding for 1 hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 790-820ºC, 820-850ºC followed by oil or water quenching or warm bath approx. 400ºC. Hardness after quenching is approx. 65 HRC.
Tempering
Tempering temperature: 150-170ºC.
Forging
Hot forming temperature: 1100-850ºC.
Specifications:
Grade: DIN 105Cr4
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers' requirements.
Delivery: 7-20 days after received deposit of T/T.
C | Mn | Si | P | S | Cr | Ni | Mo |
0.03 | 0.5 | 0.5 | 0.02 | 0.005 | 11.5~13.5 | 4.5~6.5 | 1.5~3.5 |
Mechanical behavior
State: hardening and tempering state. The supply status is typically 95 or 110 ksi, 0.2% yield strength
Extreme tensile strength: 115 ksi or more (792N / mm2)
0.2% Yield point: 110 ksi or more (758 N / mm2)
Elongation: 15%
V-notch impact strength (-10 ° C): 78 Joules (60ft-lbf)
Hardness: 33%