Alloy Carbon Steel Bar, 1.2764 Mat Number
Wuxi Taixie Metal Material Co., Ltd.- Technique:Hot Rolled
- Composition:Ferrous Steel Scrap
- Standard:AISI, ASTM, DIN, JIS, GB
- Type:Special Steel Bar
- Shape:Bar
- Surface Treatment:Polished
Base Info
- Transport Package:Woven Bag, Wooden Box
- OEM:Yes
- Delivery Time:5~10 Working Days
- Yield Strength:225
- Certificate:ISO SGS
- Poisson′s Ratio:0.25~0.33
- Strength:375-500
- Elongation:25
- Application:Tool Steel Bar
- Special Use:High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
- Model NO.:ASB9
- Specification:ISO SGS
- Trademark:Taixie
- Origin:Wuxi, Jiangsu
- HS Code:7507120000
- Production Capacity:10000tons,Y
Description
Basic Info.
Model NO. ASB9 Special Use High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel Application Tool Steel Bar Elongation 25 Strength 375-500 Poisson′s Ratio 0.25~0.33 Certificate ISO SGS OEM Yes Delivery Time 5~10 Working Days Yield Strength 225 Transport Package Woven Bag, Wooden Box Specification ISO SGS Trademark Taixie Origin Wuxi, Jiangsu HS Code 7507120000 Production Capacity 10000tons/YProduct Description
Key Specifications/Special Features:Description:
Special structural steel
Applications:
Special purpose production
Parts of larger cross-sections where higher toughness is demanded, for gears, crankshafts
Physical properties (avarage values) at ambient temperature:
Modulus of elasticity: 210103 x N/mm2
Density: 7.80g/cm3
Soft annealing:
Heat to 620 to 660oC, cool slowly in furnace
This will produce a maximum Brinell hardness of 255
Intermediate annealing:
Temperature: 600 to 630oC
Carburizing:
Temperature: 860 to 890oC
Hardening:
Harden from a temperature of 780 to 810oC followed by oil quenching or thermal bath at 180 to 220oC
Tempering:
Tempering temperature: 150 to 180oC
Forging:
Hot forming temperature: 1050 to 850oC
C | Mn | Si | P | S | Cr | Ni | Mo |
0.03 | 0.5 | 0.5 | 0.02 | 0.005 | 11.5~13.5 | 4.5~6.5 | 1.5~3.5 |
Mechanical behavior
State: hardening and tempering state. The supply status is typically 95 or 110 ksi, 0.2% yield strength
Extreme tensile strength: 115 ksi or more (792N / mm2)
0.2% Yield point: 110 ksi or more (758 N / mm2)
Elongation: 15%
V-notch impact strength (-10 ° C): 78 Joules (60ft-lbf)
Hardness: 33%