321 Stainless Steel Round Bar Manufacturer, Suppliers and Stockists in S32100 Round Bar and S32109 Round Bar.
Wuxi City Ge Ming Sheng Steel Trading Co., Ltd- Type：Stainless Steel Bars
- Standard：ASTM
- Grade：300 Series
- Certification：AISI
- Shape：Round
- Technique：Cold Rolled
Base Info
- Surface Treatment：Bright
- Transport Package：Wooden Box
- Specification：OD 6-630mm
- Production Capacity：50000kgs
Description
Detail Information of Our Stainless Steel Bar Products
About 321 Stainless Steel
Alloy 321 (UNS S32100) is stabilized stainless steel plate which offers as its main advantage an excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800 to 1500°F (427 to 816°C). Alloy 321 stainless steel plate is stabilized against chromium carbide formation by the addition of titanium.
Alloy 321 stainless steel plate is also advantageous for high temperature service because of its good mechanical properties. Alloy 321 stainless steel plate offers higher creep and stress rupture properties than Alloy 304 and, particularly, Alloy 304L, which might also be considered for exposures where sensitization and intergranular corrosion are concerns.
Alloy 321 (UNS S32100) is titanium stabilized austenitic stainless steel plate with good general corrosion resistance. It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 - 1500°F (427 - 816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness.
Alloy 321H (UNS S 32109) stainless steel plate is the higher carbon (0.04 - 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000oF (537°C). In most instances, the carbon content of the plate enables dual certification.
Alloy 321 stainless steel plate cannot be hardened by heat treatment, only by cold working. It can be easily welded and processed by standard shop fabrication practices.
Composition of 321 stainless steel
Typical compositional ranges for grade 321 stainless sheets of steel are given in table 1.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 321 | min. max | - 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 | - | 9.0 12.0 | 0.10 | Ti=5(C+N) 0.70 |
| 321H | min. max | 0.04 0.10 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 | - | 9.0 12.0 | - | Ti=4(C+N) 0.70 |
| 347 | min. max | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 | - | 9.0 13.0 | - | Nb=10(C+N) 1.0 |
Mechanical Properties of 321 stainless steel
Typical mechanical properties for grade 321 stainless sheets of steel are given in table 2.
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50 mm) min | Hardness | |
|---|---|---|---|---|---|
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 321 | 515 | 205 | 40 | 95 | 217 |
| 321H | 515 | 205 | 40 | 95 | 217 |
| 347 | 515 | 205 | 40 | 92 | 201 |
Applications of 321 stainless steel
Typical applications include:
- Aircraft exhaust manifolds
- Expansion joints
- Bellows
- Furnace parts
- Heating element tubing
- Heat Exchangers
- Woven or welded screens for high-temperature mineral processing
- Spiral Welded tube for burner pipes and flues