• Model NO.：1.3247, M42, SKH59, W2Mo9Cr4VCo8
• Special Use：Used for Cutter in Common Use
• Application：Tool Steel Bar
• The Epidermis：Black or Silver Material
• Thickness：5mm-800mm
• Length：100mm-5800mm
• Width：50mm-22000mm
• Grade：1.3247, M42, Skh59, W2mo9cr4vco8
• Annealed Hardness：255hbs
• Certificate：ISO , Mill Certificate
• Test：SGS , Ut 100% , Element Testing
• Payment：30% Deposit, Blance by L,C at Sight or T,T
• Delivery Quantity：Include MOQ
• Transport Package：Export Standard Packing or Customers′demand
• Specification：DIN JIS AISI GB
• Trademark：CF STEEL
• Origin：China
• HS Code：7225
• Production Capacity：1000t,Month

Basic Info.

Model NO. 1.3247, M42, SKH59, W2Mo9Cr4VCo8 Special Use Used for Cutter in Common Use Application Tool Steel Bar The Epidermis Black or Silver Material Thickness 5mm-800mm Length 100mm-5800mm Width 50mm-22000mm Grade 1.3247, M42, Skh59, W2mo9cr4vco8 Annealed Hardness 255hbs Certificate ISO / Mill Certificate Test SGS / Ut 100% / Element Testing Payment 30% Deposit, Blance by L/C at Sight or T/T Delivery Quantity Include MOQ Transport Package Export Standard Packing or Customers′demand Specification DIN JIS AISI GB Trademark CF STEEL Origin China HS Code 7225 Production Capacity 1000t/Month

Product Description

1.3247/M42/SKH59 High Speed Alloy Tool Steel Plate

 
Application:
Used  for cutters in common use.
1) This for high speed steel, tungsten steel adaptable to make strong cutting use wear-resisting, resistance to impact a variety of tools, advanced punching die, screw die;
2) Is need toughness and shape complex tools, milling cutter, drill, etc

Feature:
1) Die steel for manufacturing strong cutting with wear-resistant, resistant to impact a variety of tools;
2) Specially for hard and hi-speed cutting; 

Preheat temperature: 730-730 °C

Quenching temperature: 1190-1210 °C

Tempering temperature: Cold drawn, hardness 285 HBS,Cold drawn after annealing condition, hardness 277 HBS;

Heat treatment
Fire: isothermal annealing temperature is 800 ~ 880 °C, with 10 ~ 20 °C, the dHr furnace cooling to about 600 °C, hardness above HB269;

Chemical composition(%)

C	Si	Mn	P	S	Cr	V	W	Mo	Co
1.~1.15	≥0.65	≥0.40	≤0.030	≤0.030	3.50~4.50	0.95~1.35	1.15~1.85	9.0~10.0	7.50~8.50

 
Quenching methods: oil quenching, air cooling or salt bath quenching;

Delivery state: forging parts produced with continuous casting and electro-slag re-melting process; rolled as annealed, bright and quenched/tempered steel bars.

Listed specifications are only typical grades; products of required specifications can be developed/produced per international, Chinese or industry standards, or based on agreements with customers.

Packing: Standard export packing or according to customers' request.

Delivery:
For abundant stock, 15-20 days.
For customized products, 30-50 days.