- Transport Package:Waterproof Paper with Steel Strip Strapping;Contai
- Specification:OD: 13.7mm-1020mm, WT: 2.11mm-100mm
- Trademark:HYT
- Origin:China
- HS Code:7306309000
- Production Capacity:600000 Tons Per Year
Steel Grade | Chemical Composition % | Tensile Strength (MPa) | Yield Strength (MPa) |
| C | Mn | P | S | Cu | Ni | Cr | Mo | MIN |
L245/B | ≤0.28 | ≤1.20 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥415 | ≥245 |
L290/X42 | ≤0.28 | ≤1.30 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥415 | ≥290 |
L320/X46 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥435 | ≥320 |
L360/X52 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥460 | ≥360 |
L390/X56 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥490 | ≥390 |
L415/X60 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥520 | ≥415 |
L450/X65 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥535 | ≥450 |
L485/X70 | ≤0.28 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥570 | ≥485 |
The following are chemical compositions and mechnical properties of API 5L PSL1 Welded Steel Pipes:
Steel Grade | Chemical Composition % | Tensile Strength (MPa) | Yield Strength (MPa) |
| C | Mn | P | S | Cu | Ni | Cr | Mo | MIN |
L245/B | ≤0.26 | ≤1.20 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥415 | ≥245 |
L290/X42 | ≤0.26 | ≤1.30 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥415 | ≥290 |
L320/X46 | ≤0.26 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥435 | ≥320 |
L360/X52 | ≤0.26 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥460 | ≥360 |
L390/X56 | ≤0.26 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥490 | ≥390 |
L415/X60 | ≤0.26 | ≤1.40 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥520 | ≥415 |
L450/X65 | ≤0.26 | ≤1.45 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥535 | ≥450 |
L485/X70 | ≤0.26 | ≤1.65 | ≤0.030 | ≤0.030 | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.15 | ≥570 | ≥485 |
The following are chemical compositions and mechnical properties of API 5L PSL2 Seamless & Welded Steel Pipes:
Steel Grade | Chemical Composition % | Tensile Strength (MPa) | Yield Strength (MPa) |
| C | Si | Mn | P | S | RANGE |
L245R/BR | ≤0.24 | ≤0.40 | ≤1.20 | ≤0.025 | ≤0.015 | 415~760 | 245~450 |
L290R/X42R | ≤0.24 | ≤0.40 | ≤1.20 | ≤0.025 | ≤0.015 | 415~760 | 290~495 |
L245N/BN | ≤0.24 | ≤0.40 | ≤1.20 | ≤0.025 | ≤0.015 | 415~760 | 245~450 |
L290N/X42N | ≤0.24 | ≤0.40 | ≤1.20 | ≤0.025 | ≤0.015 | 415~760 | 290~495 |
L320N/X46N | ≤0.24 | ≤0.40 | ≤1.40 | ≤0.025 | ≤0.015 | 435~760 | 320~525 |
L360N/X52N | ≤0.24 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 460~760 | 360~530 |
L390N/X56N | ≤0.24 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 490~760 | 390~545 |
L415N/X60N | ≤0.24 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 520~760 | 415~565 |
L245Q/BQ | ≤0.18 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 415~760 | 245~450 |
L290Q/X42Q | ≤0.18 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 415~760 | 290~495 |
L320Q/X46Q | ≤0.18 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 460~760 | 360~530 |
L360Q/X52Q | ≤0.18 | ≤0.45 | ≤1.50 | ≤0.025 | ≤0.015 | 460~760 | 360~530 |
L390Q/X56Q | ≤0.18 | ≤0.45 | ≤1.50 | ≤0.025 | ≤0.015 | 490~760 | 390~545 |
L415Q/X60Q | ≤0.18 | ≤0.45 | ≤1.70 | ≤0.025 | ≤0.015 | 520~760 | 415~565 |
L450Q/X65Q | ≤0.18 | ≤0.45 | ≤1.70 | ≤0.025 | ≤0.015 | 535~760 | 450~600 |
L485Q/X70Q | ≤0.18 | ≤0.45 | ≤1.80 | ≤0.025 | ≤0.015 | 570~760 | 485~635 |
L555Q/X80Q | ≤0.18 | ≤0.45 | ≤1.90 | ≤0.025 | ≤0.015 | 625~825 | 555~705 |
The following are chemical compositions and mechnical properties of API 5L PSL2 Welded Steel Pipes:
Steel Grade | Chemical Composition % | Tensile Strength (MPa) | Yield Strength (MPa) |
| C | Si | Mn | P | S | RANGE |
L245M/BM | ≤0.22 | ≤0.45 | ≤1.20 | ≤0.025 | ≤0.015 | 415~760 | 245~450 |
L290M/X42M | ≤0.22 | ≤0.45 | ≤1.30 | ≤0.025 | ≤0.015 | 415~760 | 290~495 |
L320M/X46M | ≤0.22 | ≤0.45 | ≤1.30 | ≤0.025 | ≤0.015 | 460~760 | 360~530 |
L360M/X52M | ≤0.22 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 460~760 | 360~530 |
L390M/X56M | ≤0.22 | ≤0.45 | ≤1.40 | ≤0.025 | ≤0.015 | 490~760 | 390~545 |
L415M/X60M | ≤0.12 | ≤0.45 | ≤1.60 | ≤0.025 | ≤0.015 | 520~760 | 415~565 |
L450M/X65M | ≤0.12 | ≤0.45 | ≤1.60 | ≤0.025 | ≤0.015 | 535~760 | 450~600 |
L485M/X70M | ≤0.12 | ≤0.45 | ≤1.70 | ≤0.025 | ≤0.015 | 570~760 | 485~635 |
L555M/X80M | ≤0.12 | ≤0.45 | ≤1.85 | ≤0.025 | ≤0.015 | 625~825 | 555~705 |
L625M/X90M | ≤0.10 | ≤0.55 | ≤2.10 | ≤0.020 | ≤0.010 | 695~915 | 625~775 |
L690M/X100M | ≤0.10 | ≤0.55 | ≤2.10 | ≤0.020 | ≤0.010 | 760~990 | 690~840 |
L830M/X120M | ≤0.10 | ≤0.55 | ≤2.10 | ≤0.020 | ≤0.010 | 915~1145 | 830~1050 |
M:thermo-mechanically deformed and subsequent controlled cooled ( TMCP)
R:hot rolled
Q:quenching and tempering
N:normalizing